T1  - Cation distribution in Cu2ZnSnSe4, Cu2FeSnS4 and Cu2ZnSiSe4 by multiple‐edge anomalous diffraction
Y1  - 2020-12-07
VL  - 76
IS  - 6
SP  - 1027
EP  - 1035
JF  - Acta Crystallographica Section B
DO  - 10.1107/S2052520620013384
DO  - 10.23689/fidgeo-4116
PB  - International Union of Crystallography
N2  - Multiple‐Edge Anomalous Diffraction (MEAD) has been applied to various quaternary sulfosalts belonging to the adamantine compound family in order to validate the distribution of copper, zinc and iron cations in the structure. Semiconductors from this group of materials are promising candidates for photovoltaic applications. Their properties strongly depend on point defects, in particular related to cation order–disorder. However, Cu+, Zn2+ and Fe2+ have very similar scattering factors and are all but indistinguishable in usual X‐ray diffraction experiments. Anomalous diffraction utilizes the dependency of the atomic scattering factors f′ and f′′ of the energy of the radiation, especially close to the element‐specific absorption edges. In the MEAD technique, individual Bragg peaks are tracked over an absorption edge. The intensity changes depending on the structure factor can be highly characteristic for Miller indices selected for a specific structural problem, but require very exact measurements. Beamline KMC‐2 at synchrotron BESSY II, Berlin, has been recently upgraded for this technique. Anomalous X‐ray powder diffraction and XAFS compliment the data. Application of this technique confirmed established cation distribution in Cu2ZnSnSe4 (CZTSe) and Cu2FeSnS4 (CFTS). In contrast to the literature, cation distribution in Cu2ZnSiSe4 (CZSiSe) is shown to adopt a highly ordered wurtz‐kesterite structure type.
N2  - Multiple‐Edge Anomalous Diffraction (MEAD) has been applied to various quaternary sulfosalts belonging to the adamantine compound family in order to validate the distribution of copper, zinc and iron cations in the structure. Application of this technique confirms established cation distribution in Cu2ZnSnSe4 (CZTSe) and Cu2FeSnS4 (CFTS), but in Cu2ZnSiSe4 (CZSiSe) the cation distribution is shown to adopt a highly ordered wurtz‐kesterite structure type in contrast to the literature. image
UR  - http://resolver.sub.uni-goettingen.de/purl?gldocs-11858/8456
ER  -