Quantitative Analysis of the Misorientation Distribution After the Recrystallisation of Tensile Deformed Copper Single Crystals

Abstract

Recrystallisation experiments in tensile deformed <100>- and <111>-oriented single crystals of high purity copper yielded very accurate information about the orientations of recrystallised grains and deformation microstructure. For a statistical evaluation of the orientation relationships between the dominant recrystallised grains and the deformation microstructure the misorientation distribution function was calculated. The most frequently occurring orientation relationships can be described by coincidence relationships. Always several coincidence relationships are needed to characterise the results. The specimen treatment strongly influences the occurrence of the individual coincidence orientation relationships. A particularly preferred growth of grains with a 30° or 40° <111> orientation relationship was not observed.